SARPOL SF

Mixture

Specific gravity @ 25 °C 1.61

Flash point °C >100

Properties of Hardening

Working Time (200 g mass), ISO 9514, minutes: 45

Coating time, at 25 °C, hours: 2-24

Touch-drying time, at 25 °C, hours: 4

Functional drying time, at 25 °C, hours: 12

Time Polymerization Complete, at 25 °C, hours: 48

Coverage

Spray application, minimum thickness of 300 microns, yield is 1.77 m²/kg, excluding waste and scrap.

Dilution not allowed

GENERAL INFORMATION

This product is not recommended for use in oxygen-rich and/or pure oxygen systems and should not be selected as a sealant for chlorine or other strong oxidizing materials.

For information on the safe handling of this product, consult the safety data sheet (SDS).

Surface Preparation

A surface preparation is important for long-term product performance. Parameters may vary depending on the severity of the application, expectations for durability, and initial conditions of the substrates to be treated.

1. Remove any dirt, oil, grease etc. with a suitable detergent.
2. Every irregularity, splash or weld witness and every other surface roughness, must be leveled and flattened; every indentation or porosity must be grouted and leveled. Every protrusion, edge or joint, must be leveled with a minimum radius of 3mm and every corner must also be rounded with the same characteristics.
3. Sandblast the entire surface to be treated with an angular grit to a roughness of 50-70 microns, and a blasting grade close to White Metal (SIS SA 2½ /SSPC-SP 10). For immersion applications, a blasting grade equal to White Metal is required (SIS SA 3/SSPC-SP 5).
4. After blasting, the metal surface should be cleaned with a residue-free cleaner or acetone to remove dust and contaminants. Clean, dry compressed air can also be used to remove dust and contaminants. The surface should be coated before reoxidation occurs.

Mode of Application:

1. Film thickness for coating: 400 micron (minimum). It is recommended to apply a minimum of 2 layers to avoid micro-pitting.
2. Application temperature for surface and environment: 15-30 °C.
3. Relative humidity: <85 %; Surface temperature should always be above the dew point by at least 3 °C.
4. Spray systems:

• Airless sprayer for abrasive two-pack products with compression ratio of at least 45:1.
• Nozzle 0.015” - 0.019”; width 50-60°, dependent on the part to be coated.
• Pressione all’ugello: 210 bar minimo. Temperatura del prodotto ≥25 °C.

Le seconde mani di ricopertura devono essere eseguite una volta che lo strato di prodotto è gellificato ma non polimerizzato, entro il “tempo di ricopertura”. Se questo tempo viene superato, bisogna abradere leggermente la superficie e pulire con MEK per eliminarne i residui.

Check:

• When the application is just completed, visually check for untreated porosity.
• Once the coating has cured, repeat the visual inspection to confirm the absence of untreated areas and porosity or mechanical damage.
• Check the coating thickness, above all in critical areas.

Repairs

Any untreated area or porosity or area with little thickness detected should be restored or repaired by applying additional product, after light abrasion and cleaning of the surface.

Cleaning

Pulire immediatamente le attrezzature dopo l’uso con un solvente quale acetone o alcol isopropilico. Una volta indurito, il prodotto si può rimuove solo meccanicamente