SAROPLAST T250 A&B

Properties of Part A:

Densità @ 25 C, ISO 1675, g/cm³                        1.55

Viscosità BRF, ISO 2555, @ 25°C, 10 rpm           230

Viscosità BRF, ISO 2555, @ 25°C, 1 rpm             1300

Properties of Part B:

Densità @ 25 °C, ISO 1675, g/cm³                       1.53

Viscosità BRF, ISO 2555, @ 25°C, 10 rpm           170

Viscosità BRF, ISO 2555, @ 25°C, 1 rpm             900

Properties of Compound A + B:

Densità @ 25 °C, ISO 1675, g/cm³                       1.55

Properties of Hardening

Gel time, ASTM D2471 minutes 35

Tempo di inizio presa, a 25 °C, ore:                      8 – 12

Tempo di fine presa, a 25 °C, ore:                        24

Messa in esercizio, a 25 °C, ore:                          72

Coverage

Applicazione a Spatola, spessore minimo di 1mm, la resa è di 0.65 m² / kg, escludendo sprechi e sfridi.

GENERAL INFORMATION

This product is not recommended for use in oxygen-rich and/or pure oxygen systems and should not be selected as a sealant for chlorine or other strong oxidizing materials.

For information on the safe handling of this product, consult the safety data sheet (SDS).

Surface Preparation

A surface preparation is important for long-term product performance. Parameters may vary depending on the severity of the application, expectations for durability, and initial conditions of the substrates to be treated.

1. Remove any dirt, oil, grease etc. with a suitable detergent.
2. Every irregularity, splash or weld witness and every other surface roughness, must be leveled and flattened; every indentation or porosity must be grouted and leveled. Every protrusion, edge or joint, must be leveled with a minimum radius of 3mm and every corner must also be rounded with the same characteristics.
3. Sandblast the entire surface to be treated with an angular grit to a roughness of 50-70 microns, and a blasting grade close to White Metal (SIS SA 2½ /SSPC-SP 10). For immersion applications, a blasting grade equal to White Metal is required (SIS SA 3/SSPC-SP 5).
4. After blasting, the metal surface should be cleaned with a residue-free cleaner or solvent to remove dust and contaminants. Clean, dry compressed air can also be used to remove dust and contaminants. The surface should be coated before reoxidation occurs.

Mode of Application:

1. Miscelare i due componenti, opportunamente pesa nelle quantità previste da rapporto di miscelazione, per circa 3min.
2. Film thickness 1mm.
3. Application temperature for surface and environment: 15-30 °C.
4. Relative humidity: <85 %; Surface temperature should always be above the dew point by at least 3 °C.
5. All untreated areas or areas with limited thickness must be restored by applying further product before installing the covering to be adhered

Cleaning

Clean equipment immediately after use with a solvent such as acetone or isopropyl alcohol. Once cured, the product can only be removed mechanically.